Near room temperature magnetic entropy changes in as-cast Gd_(100-x)Mn_x (x = 0, 5,10,15, and 20 at.%) alloys

机译：接近室温的铸造Gd_（100-x）Mn_x（x = 0、5、10、15和20 at。％）合金的磁熵变

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

A series of Gd_(100-x)Mn_x (x = 0,5,10,15, and 20 at.%) alloys were prepared by arc-melting. The Curie temperature (T_c) associated with the ferromagnetic-paramagnetic transitions, derived from M-T curves, show decrease in T_c for as-cast alloys (~279 K) as compared to as-cast Gd (~292 K). No appreciable decrease in the |ΔS_M|_(max) values ~4.6 J/kgK (0-2T) and ~8.6J/kg K (0-5T) were observed upon alloying Gd with Mn up to x < 15 at.%. Refrigerant capacity (q) showed negligible variation ~195 J/kg (0-2 T) and ~450J/kg (0-5 T) with increasing Mn (up to x< 15 at.%) content.
机译：通过电弧熔化制备了一系列Gd_（100-x）Mn_x（x = 0、5、10、15和20 at。％）合金。由M-T曲线得出的与铁磁-顺磁转变相关的居里温度（T_c）与铸态Gd（〜292 K）相比，铸态合金（〜279 K）的T_c降低。在将Gd与Mn合金化至x <15 at。％时，未观察到|ΔS_M| _（max）值〜4.6 J / kgK（0-2T）和〜8.6J / kg K（0-5T）的可观降低。 。随着锰含量的增加（最多x <15 at。％），制冷剂容量（q）表现出的〜195 J / kg（0-2 T）和〜450J / kg（0-5 T）的变化可以忽略不计。