首页> 外文期刊>Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics >Effect of Cr_7C_3 on the mechanical, thermal, and electrical properties of Cr_2AlC
【24h】

Effect of Cr_7C_3 on the mechanical, thermal, and electrical properties of Cr_2AlC

机译：Cr_7C_3对Cr_2AlC的机械，热和电性能的影响

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

In this work, phase pure Cr_2AlC and impure Cr_2AlC with Cr_7C_3 have been fabricated to investigate the mechanical, thermal, and electrical properties. The thermal expansion coefficient is determined as 1.25 x 10~(-5) K~(-1) in the temperature range of 25-1200 °C. The thermal conductivity of the Cr_2AlC is 15.73 W/m K when it is measured at 200 °C. With increasing temperature from 25 °C to 900 °C, the electrical conductivity of Cr_2AlC decreases from 1.8 x 10~6 ?~(-1) m~(-1) to 5.6 x 10~5 ?~(-1) m~(-1).
机译：在这项工作中，已制造出具有Cr_7C_3的相纯Cr_2AlC和不纯Cr_2AlC，以研究机械，热和电性能。在25-1200°C的温度范围内，热膨胀系数确定为1.25 x 10〜（-5）K〜（-1）。在200°C下测量时，Cr_2AlC的热导率为15.73 W / mK。随着温度从25°C升高到900°C，Cr_2AlC的电导率从1.8 x 10〜6？〜（-1）m〜（-1）降低到5.6 x 10〜5？〜（-1）m〜 （-1）。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号