Effect of milling on the magnetic properties of Al-Mn obtained by mechanical alloying

机译：铣削对机械合金化获得的Al-Mn磁性的影响

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Al-Mn powders were prepared to obtain the compound Mn_(42)Al_(58) by mechanical alloying. The powders were milled during different periods (1 h, 5 h, 11.5 h, 15 h, 20 h and 50 h) using a SPEX 8000 mixer mill in nitrogen atmosphere. The materials were characterized by X-ray diffraction (XRD) and magnetic properties at room temperature, using a vibrating sample magnetometer (VSM). XRD shows partial transformation to α-Mn after only 1 h of milling and a mixture of α-Mn and β-Mn after 11.5 h of milling and further milling resulted in transformation to β-Mn phase with a grain size of 6 nm after 50 h. The change in magnetic properties with milling time is quite dramatic, from a ferromagnetic behavior for α-Mn(Al) to paramagnetic after 11.5 h of milling and showing again ferromagnetic behavior, with a strong increase of magnetization values of 5.5 emu/g, after 50 h of milling with formation of β-Mn(Al).
机译：制备Al-Mn粉末，通过机械合金化得到化合物Mn_（42）Al_（58）。使用SPEX 8000混合机在氮气氛下，将粉末在不同的时间段（1小时，5小时，11.5小时，15小时，20小时和50小时）研磨。使用振动样品磁力计（VSM）对材料进行了X射线衍射（XRD）和室温下的磁性能表征。 XRD显示仅在铣削1小时后部分转变为α-Mn，在铣削11.5 h之后又出现α-Mn和β-Mn的混合物，进一步铣削后50转变为晶粒度为6 nm的β-Mn相H。磁性随铣削时间的变化非常显着，从铣削11.5小时后的α-Mn（Al）的铁磁行为到顺磁，并再次显示出铁磁行为，在经过铣削后，磁化强度大大提高了5.5 emu / g。研磨50小时，形成β-Mn（Al）。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号