首页> 外文期刊>Journal of Materials Science >Synthesis and characterization of TiO2-incorporated silica foams
【24h】

Synthesis and characterization of TiO2-incorporated silica foams

机译：TiO2掺入的二氧化硅泡沫的合成与表征

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Titania-incorporated silica (TiO2-SiO2) porous materials have great applications in diverse areas. In this work, TiO2-SiO2 porous materials with tunable Si/Ti molar ratio (R) have been successfully prepared through a one-pot method under a near-neutral condition. With decreasing Si/Ti R, a phase transition from a macroporous foam-like structure to mesostructure is observed. The resultant TiO2-SiO2 porous materials possess large surface areas and high pore volumes. In addition, the titania species are homogenously dispersed in silica matrix when Si/Ti R a parts per thousand yen 10. Our contribution provides a convenient method to synthesize TiO2/SiO2 porous materials with very large pore size, high pore volume, and relatively high titania content well dispersed in the silica wall framework.
机译：掺有二氧化钛的二氧化硅（TiO2-SiO2）多孔材料在各个领域都有广泛的应用。在这项工作中，已经通过在近中性条件下的一锅法成功地制备了具有可调的Si / Ti摩尔比（R）的TiO2-SiO2多孔材料。随着Si / Ti R的减少，观察到从大孔泡沫状结构到介观结构的相变。所得的TiO 2 -SiO 2多孔材料具有大的表面积和高的孔体积。另外，当Si / Ti R为千分之十时，二氧化钛物种均匀地分散在二氧化硅基质中。我们的贡献为合成具有非常大的孔径，大的孔体积和相对较高的孔径的TiO2 / SiO2多孔材料提供了一种便捷的方法。二氧化钛含量很好地分散在二氧化硅壁框架中。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号