Well-aligned anatase and rutile TiO2 nanorods and nanotubes with a diameter of about 80-130 nm have successfully been fabricated via sol-gel template method. The prepared samples were characterized by using thermogravimetric (TG) and differential thermal analysis (DTA), X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and energy dispersive X-ray spectroscopy (EDS). The XRD results indicated that the TiO2 nanorods were crystallized in the anatase and rutile phases, after annealing at 400-800 degrees C for different periods of time from 0.2 to 10 h.
机译：通过溶胶-凝胶模板法成功制备了取向良好的锐钛矿型和金红石型TiO2纳米棒和直径约80-130 nm的纳米管。使用热重（TG）和差热分析（​​DTA），X射线衍射（XRD），扫描电子显微镜（SEM），透射电子显微镜（TEM）和能量色散X射线光谱（EDS）对制备的样品进行表征）。 X射线衍射（XRD）结果表明，TiO2纳米棒在400〜800℃退火0.2至10h的不同时间后，在锐钛矿和金红石相中结晶。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号