首页> 外文期刊>Journal of Materials Science >Growth of hydrophobic TiO_2 on wood surface using a hydrothermal method
【24h】

Growth of hydrophobic TiO_2 on wood surface using a hydrothermal method

机译：水热法在木材表面生长疏水性TiO_2

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Hydrophobic titanium dioxide (TiO_2) was successfully grown on a wood surface using a hydrothermal method. Energy dispersive X-ray spectroscopy (EDS), Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), and water contact angle (WCA) were employed to characterize the features of grown TiO_2 and its hydrophobicity. EDS, XRD, and FTIR proved that anatase TiO_2 chemically bonded to the wood surface through the combination of hydrogen groups during the hydrothermal process. The values of WCAs manifested that the hydrophobicity of the treated wood was mainly dependent on specific reaction conditions, especially on reaction pH value and hydrothermal temperature. The highest WCA reached 154° when the hydrothermal temperature was 130 °C. The treated wood thus possessed a superhydrophobic surface.
机译：使用水热法成功地在木材表面上生长了疏水性二氧化钛（TiO_2）。利用能量色散X射线能谱（EDS），傅立叶变换红外光谱（FTIR），X射线衍射（XRD）和水接触角（WCA）来表征生长的TiO_2的特征及其疏水性。 EDS，XRD和FTIR证明，在水热过程中，锐钛矿TiO_2通过氢基团的化学键结合到木材表面。 WCA的值表明，处理过的木材的疏水性主要取决于特定的反应条件，特别是取决于反应的pH值和水热温度。当水热温度为130°C时，最高WCA达到154°。因此，经处理的木材具有超疏水表面。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号