摘要

Ta-based bulk metallic glasses with high strength (2.7 GPa) and hardness (9.7 GPa), high elastic modulus (170 GPa) and high density (12.98 g/mm ~3) were developed. The best glass forming ability so far for a Ta-Ni-Co system reaches a critical diameter of 2 mm by the copper mold casting method. It shows an exceptionally high glass transition temperature of 983 K and a high crystallization temperature up to 1023 K. The unique mechanical and physical properties make them a promising high strength material.
机译：开发了具有高强度（2.7 GPa）和硬度（9.7 GPa），高弹性模量（170 GPa）和高密度（12.98 g / mm〜3）的Ta基块状金属玻璃。迄今为止，对于Ta-Ni-Co系统而言，最佳的玻璃成型能力通过铜模铸法达到了2 mm的临界直径。它具有983 K的极高玻璃化转变温度和高达1023 K的高结晶温度。独特的机械和物理性能使其成为有前途的高强度材料。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号