The distributions of coercivities and magnetic interactions in a set of polycrystalline Ni_(0.8)Fe_(0.2)/FeMn bilayers have been determined using the first-order reversal curve (FORC) formalism. The thickness of the permalloy (Py) film was fixed at 10 nm (nominal), while that of the FeMn film varied within the range 0-20nm. The FORC diagrams of each bilayer displayed two clearly distinguishable regions. The main region was generated by Py particles whose coercivities were enhanced in comparison with those in which the FeMn film was absent (sample O). The minor region was produced by Py particles with coercivities similar to or slightly higher than those of particles in the Py film of sample O. Each sample presented two distributions of interaction fields, one for each region, and both were centred slightly below the exchange-bias field, thus indicating a prevalence of magnetizing interactions. These results are consistent with a grain size distribution in the Py layer and the presence of uncompensated antiferromagnetic moments.