首页> 外文期刊>Journal of Physics, D. Applied Physics: A Europhysics Journal >TIPS-DBC small molecule O-FETs fabricated by evaporation and solution processing
【24h】

TIPS-DBC small molecule O-FETs fabricated by evaporation and solution processing

机译：通过蒸发和溶液处理制造的TIPS-DBC小分子O-FET

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The performance of organic field effect transistors using the small molecule, tri-isopropyl- silane-di-benzo chrysene (TIPS-DBC) is reported. The field effect mobility FE is found to depend on the deposition conditions, which affect the morphology of the film. A mobility in the range of 1.5×10 ~(-6) to 2.4×10 ~(-4)cm ~2V ~(-1)s ~(-1) is obtained from the evaporated films depending on the substrate treatment and deposition temperature, while films deposited by solution-processing techniques yield mobilities in the range of 0.7×10 ~(-3) to 1.5×10 ~(-3)cm ~2V ~(-1)s ~(-1). The enhanced performance in polycrystalline solution-processed coatings and its relationship to crystallite size is an important parameter in the design of high-performance devices based on small molecules.
机译：报道了使用小分子三异丙基硅烷-二苯并菲（TIPS-DBC）的有机场效应晶体管的性能。发现场效应迁移率FE取决于沉积条件，该沉积条件影响膜的形态。根据基底处理和沉积，从蒸发的膜获得在1.5×10〜（-6）至2.4×10〜（-4）cm〜2V〜（-1）s〜（-1）范围内的迁移率。通过固溶处理技术沉积的薄膜产生的迁移率范围为0.7×10〜（-3）至1.5×10〜（-3）cm〜2V〜（-1）s〜（-1）。多晶溶液处理涂层的增强性能及其与微晶尺寸的关系，是基于小分子的高性能器件设计中的重要参数。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号