首页> 外文期刊>RSC Advances >Hydrated FePO4 nanoparticles supported on P-doped RGO show enhanced ORR activity compared to their dehydrated form in an alkaline medium
【24h】

Hydrated FePO4 nanoparticles supported on P-doped RGO show enhanced ORR activity compared to their dehydrated form in an alkaline medium

机译：与碱性介质中的脱水形式相比，在P掺杂Rgo上负载的水合FEPO4纳米颗粒显示出增强的ORR活性

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

One-step hydrothermal growth of FePO4 nanoparticles (15-25 nm) uniformly decorated on the P-doped reduced graphene oxide (PRGO) was studied for oxygen reduction reaction (ORR) activity. The role of lattice water in the enhancement of catalytic activity in the hydrated FePO4 center dot 2H(2)O with respect to its dehydrated form in the alkaline medium was contested. The hydrodynamic LSV at 1600 rpm in alkaline medium (0.1 M KOH electrolyte) indicates an increase in the cathodic current density of the PRGO supported FePO4 center dot 2H(2)O catalyst, which reaches as high as 5.8 mA cm(-2), close to the best known commercially available Pt/C catalyst. The stability in terms of retention of activity after 22 000 s with the hydrated form was found to be 90.7% which is 26.7% higher than that of the dehydrated form.
机译：研究了在P掺杂的石墨烯氧化物（PRGO）上均匀地装饰的FEPO4纳米颗粒（15-25nm）的一步水热生长用于氧还原反应（ORR）活性。 果酱在碱性培养基中脱水形式的水合FEPO4中心点2H（2）O中催化活性提高的作用。 1600rpm的碱性介质（0.1M KOH电解质）的流体动力学LSV表明PRGO负载的FEPO4中心点2H（2）o催化剂的阴极电流密度的增加，该催化剂高达5.8 mA cm（-2）， 接近最佳已知的商业上可用的Pt / C催化剂。 发现具有水合形式的22 000秒后活性保留的稳定性为90.7％，比脱水形式高出26.7％。

著录项

  • 来源
    《RSC Advances》 |2019年第42期|共5页
  • 作者

  • 作者单位
  • 收录信息
  • 原文格式 PDF
  • 正文语种 eng
  • 中图分类 化学;
  • 关键词

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号