摘要

The corrosion behaviors of 13Cr martensitic steel under different CO2 partial pressures (4-28 MPa) were investigated by weight loss tests and surface characterizations. The results show that the corrosion rate of 13Cr steel shows a sharp increase under higher CO2 pressure (28 MPa), which reached approximately 20-180 times as large as those under lower CO2 pressures (4-12 MPa). Under the lower CO2 pressures, a single-layered Cr(OH)(3) passive film forms and completely covers the steel surface. However, when the CO2 pressure reaches 28 MPa, a very different corrosion film which contains an inner Cr(OH)(3) passive layer and an outer FeCO3 layer forms, and the inner passive layer shows local damage. This phenomenon can be explained by the lower pH (similar to 2.75) and the higher H2CO3 concentration in the solution under the higher CO2 pressure.
机译：通过减肥试验和表面表征研究了不同CO 2分压（4-28MPa）下的13Cr马氏体钢的腐蚀行为。 结果表明，13Cr钢的腐蚀速率显示在较高的CO 2压力（28MPa）下急剧增加，其达到较低的CO 2压力（4-12MPa）的大约20-180倍。 在较低的CO 2压力下，单层Cr（OH）（3）无源膜形成并完全覆盖钢表面。 然而，当CO2压力达到28MPa时，含有内部Cr（OH）（3）无源层和外部FECO3层形式的非常不同的腐蚀膜，并且内部被动层显示出局部损坏。 这种现象可以通过较低的pH（类似于2.75）和溶液中较高的CO 2压力下的H 2 CO 3浓度来解释。

著录项

  • 来源
    《RSC Advances》 |2019年第66期|共7页
  • 作者

  • 作者单位
  • 收录信息
  • 原文格式 PDF
  • 正文语种 eng
  • 中图分类 化学;
  • 关键词

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号