A newly developed Fe85B12La3 amorphous alloy with outstanding magneto-caloric effect (MCE) is reported. The glass forming ability of the Fe85B12La3 ternary alloy is good enough for it to be fabricated into amorphous ribbons. Magnetic and magnetocaloric properties of the amorphous alloy were examined. The Fe85B12La3 amorphous ribbon exhibit outstading MCE of a soft magnetic amorphous alloy with the -Delta S-m(peak) value is about 1.08 Jkg(-1)K(-1) under 1 T, 1.82 Jkg(-1)K(-1) under 2 T, 2.46 Jkg(-1)K(-1) under 3 T, 3.04 Jkg(-1)K(-1) under 4 T and 3.59 Jkg(-1)K(-1) under 5 T at the Curie temperature (T-c) of 477.5 K, and the maximum adiabatic temperature rise (Delta T-ad) and the refrigeration cooling power is comparable to or even larger than those of other Fe-based metallic glass. The Fe85B12La3 amorphous alloy among the reported Fe-based amorphous alloys, indicating that the amorphous alloy is a good candidate for magnetic refrigerants near its Curie temperature.
机译：报道了新开发的Fe85b12La3非晶合金，具有出色的磁热 - 热效应（MCE）。 Fe85b12la3三元合金的玻璃成型能力足以使其制造成非晶带。 检查无定形合金的磁性和磁热性质。 Fe85b12la3无定形带表现出软磁无定形合金的MCE与-delta sm（峰值）值约为1.08 jkg（-1）k（-1），1.82 jkg（-1）k（-1） 在3吨，3.04 jkg（-1）k（-1）下的2吨，2.46 jkg（-1）k（-1）下为4 t和3.59 jkg（-1）k（-1）下方的3吨和3.59 jkg（-1） 居里温度（Tc）为477.5 k，最大绝热升温（ΔT-Ad）和制冷冷却功率比其他Fe系的金属玻璃的更大或甚至更大。 据报道的Fe-碱性合金中的Fe85B12LA3非晶合金，表明无定形合金是诸如居里温度附近的磁性制冷剂的良好候选者。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号