Preparation of Fe-MOFs by microwave-assisted ball milling for reducing Cr(VI) in wastewater

机译：通过微波辅助球磨制备Fe-Mofs，用于减少废水中的Cr（VI）

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Fe-Based metal-organic frameworks (Fe-MOFs) were prepared with trimesic acid and FeSO4 center dot 7H(2)O via a microwave-assisted ball milling approach. The structure and thermal stability of the as-prepared Fe-MOFs were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), Fourier transform infrared spectrometry (FTIR), X-ray photoelectron spectroscopy (XPS), and thermogravimetric analysis (TGA). When used to degrade 20 mg L-1 hexavalent chromium in aqueous solution, the Fe-MOFs were found to completely reduce a 100 mL solution within 120 min under natural light and a 400 mL solution within 90 min under Xe lamp irradiation. Under natural sunlight, 98% of the Cr(VI) was removed from a 40 mL solution after 40 min.
机译：通过微波辅助球铣削方法用微波辅助酸和FeSO4中心点7h（2）o制备Fe基金属骨架（Fe-Mof）。 通过X射线衍射（XRD），扫描电子显微镜（SEM），傅里叶变换红外光谱（FTIR），X射线光电子能谱（XPS）的结构和热稳定性的特征和热稳定性特征在于，扫描电子显微镜（X射线），以及热量标注 分析（TGA）。 当用于降解水溶液中的20mg L-1六价铬时，发现Fe-MOF在自然光下在120分钟内完全减少100mL溶液，并在XE灯照射下90分钟内的400ml溶液。 在自然阳光下，40分钟后，将在40ml溶液中除去98％的Cr（VI）。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号