首页> 外文期刊>Journal of Applied Polymer Science >Performance of form-stable myristic acid/polymethyl methacrylate composite phase-change material coated with nitrile butadiene rubber/polyacrylic acid layered coatings
【24h】

Performance of form-stable myristic acid/polymethyl methacrylate composite phase-change material coated with nitrile butadiene rubber/polyacrylic acid layered coatings

机译：涂有丁腈丁二烯橡胶/聚丙烯酸层涂料的形式稳定型肉体酸/聚甲基丙烯酸甲酯复合相变材料的性能

获取原文
获取原文并翻译 | 示例
       
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The aim of this work is to determine the effect of coating and blending composition of myristic acid (MA) with polymethyl methacrylate (PMMA) on the latent heat and thermal stability of phase change material (PCM). Form-stable PCM (FSPCM) was prepared by blending MA with PMMA and then coating with nitrile butadiene rubber (NBR) and polyacrylic acid (PA) layers. This is the first attempt to coat the PCM with elastomeric latex. Leakage test results showed that addition of 20 wt% PMMA to the MA and NBR-PA coating layers could eliminate leakage in sample PCM8O. Tensile test results showed that NBR-PA coating material provide sufficient strength and elasticity to hold the PCM during the phase change process. Latent heat of melting and freezing of the form stable PCM80 is 107.56 J/g and 102.26 J/g, which is comparable with other results in the literature. (c) 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019, 137, 48642.
机译：这项工作的目的是确定含有聚甲基丙烯酸甲酯（PMMA）的粉碎和混合组合物对相变材料（PCM）的潜热和热稳定性的影响。 通过用PMMA混合MA，然后用丁腈丁二烯橡胶（NBR）和聚丙烯酸（PA）层来制备形式稳定的PCM（FSPCM）。 这是第一次尝试用弹性乳胶涂覆PCM。 泄漏试验结果表明，向MA和NBR-PA涂层添加20wt％PMMA可以消除样品PCM8O中的泄漏。 拉伸试验结果表明，NBR-PA涂层材料在相变过程中提供足够的强度和弹性以保持PCM。 熔融和冻结形式稳定PCM80的潜热是107.56J / g和102.26J / g，与文献中的其他结果相当。 （c）2019 Wiley期刊，Inc.J.Phill。 聚合物。 SCI。 2019,137,48642。