首页> 外文期刊>Journal of Applied Polymer Science >Cassava bagasse as a reinforcement agent in the polymeric blend of biodegradable films
【24h】

Cassava bagasse as a reinforcement agent in the polymeric blend of biodegradable films

机译：木薯甘蔗渣作为生物降解薄膜聚合物混合物中的增强剂

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The objective of this work was to develop biodegradable films using fibrous residue from the extraction of cassava starch and to investigate its effect as a reinforcement agent in polymeric films. Micrographs (SEM) showed that the obtained films presented smooth surfaces with no cracking. The addition of fibers affected the properties of the films significantly (p 0.05), reducing water vapor permeability values (from 8.63 +/- 0.15 x 10(-11) g.m.m(-2).s(-1).Pa-1 to 3.33 +/- 0.16 x 10(-11) g.m.m(-2).s(-1).Pa-1) and increasing the maximum tensile strength (from 1.23 +/- 0.15 MPa to 7.78 +/- 0.83 MPa). These results encourage the use of cassava bagasse as a reinforcement in the production of green composites as packaging. (c) 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019, 136, 47224.
机译：这项工作的目的是开发可生物降解的薄膜，使用来自木薯淀粉的萃取的纤维残留物，并在聚合物膜中研究其作为增强剂的效果。 显微照片（SEM）表明所获得的薄膜呈现光滑表面，没有裂化。 纤维的添加显着影响薄膜的性质（P <0.05），降低水蒸气渗透率值（从8.63 +/- 0.15×10（-11）GMM（-2）.s（-1）.pa- 1至3.33 +/- 0.16 x 10（-11）GMM（-2）.s（-1）.pa-1）并增加最大拉伸强度（从1.23 +/- 0.15 MPa到7.78 +/- 0.83 MPa ）。 这些结果鼓励使用木薯甘蔗渣作为生产绿色复合材料作为包装的加固。 （c）2018 Wiley期刊，Inc.J.Phill。 聚合物。 SCI。 2019,136,47224。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号