In this article, a novel flame-retardant polyamide 6 (PA6) was prepared by introducing a halogen-free flame-retardant (OP1314). Graphite was added as a flame-retardant synergistic agent, and the flame retardancy was enhanced, especially the melt-dripping was forbidden and for the formula of PA6/12 wt % OP1314/5 wt % graphite, UL94 V-0 grade was reached. Meanwhile, the graphite is also an excellent thermal conductive filler and with the addition of 5 wt % graphite in the flame-retardant PA6 mixtures, the thermal conductivity (lambda) rose to 1.2 W/mK which was nearly three times higher than the flame-retardant PA6. Due to the good flame retardancy and improved thermal conductivity, the material could be suitable for applications in electronic and electrical devices. (C) 2018 Wiley Periodicals, Inc.
机译：在本文中，通过引入无卤素阻燃剂（OP1314）来制备新的阻燃聚酰胺6（PA6）。 将石墨加入作为阻燃协同剂中，增强阻燃性，尤其是禁止熔融滴，达到PA6 / 12wt％OP1314 / 5wt％石墨的式，达到UL94 V-0等级。 同时，石墨也是一种优异的导热填料，并在阻燃PA6混合物中加入5wt％石墨，导热率（Lambda）升至1.2W / mk，其比火焰高出三倍。 阻滞剂pa6。 由于良好的阻燃性和改善的导热系数，材料可以适用于电子和电气设备中的应用。 （c）2018 Wiley期刊，Inc。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号