A simple strategy to increase the interfacial adhesion between TiO2 nanotube layer and Ti substrate

机译：一种简单的策略，以提高TiO2纳米管层和Ti衬底之间的界面粘附

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The weak interfacial adhesion between the anodic TiO2 nanotube array (TNTA) layer and Ti substrate results in the difficulty of the subsequent applications. Here, we report an efficient strategy to enhance the adhesion of the TNTA layer to the Ti substrate. That is, after completion of the fabrication of TNTAs, anodization was further performed at 10 V for 5 min in the same electrolyte. The sample subjected to the lower voltage anodization posttreatment shows 1.5 times improvement in interfacial adhesion compared to the one without posttreatment. The enhanced interfacial adhesion can be ascribed to elimination of the residual stress at the interface. Moreover, the lower voltage posttreatment can also achieve a 45.8% increase in areal capacitance of TNTAs, which can be attributed to the increased contact area between the TNTA layer and Ti substrate. (C) 2018 Elsevier B.V. All rights reserved.
机译：阳极TiO2纳米管阵列（TNTA）层和Ti衬底之间的弱界面粘附导致随后的应用的难度。 这里，我们报告了一种有效的策略，以增强TNTA层与TI衬底的粘附性。 也就是说，在完成TNTA的制造之后，在相同的电解质中在10V下进一步进行阳极氧化5分钟。 与较低电压阳极氧化后的样品显示出界面粘附的1.5倍，与没有后术的界面粘附的改善。 增强的界面粘附可以归属于消除界面处的残余应力。 此外，较低的电压后处理还可以实现TNTA的区域电容的增加45.8％，其可以归因于TNTA层和Ti衬底之间的增加的接触面积。 （c）2018年elestvier b.v.保留所有权利。