Protecting lithium anode with LiNO3/Al2O3/PVDF-coated separator for lithium-sulfur batteries

机译：用LINO3 / AL2O3 / PVDF涂覆隔膜保护锂阳极，用于锂 - 硫磺电池

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

A modified separator with LiNO3/Al2O3/PVDF coating has been prepared to protect lithium anode and enhance the cycle performance of lithium-sulfur (Li-S) batteries. The functional coating directly contacted with lithium, and the LiNO3 absorbed in Al2O3 nano particles was released slowly, offering a durable protection to lithium. The initial discharge capacity of the cell assembled with the LiNO3/Al2O3/ PVDF-coated separator is 1283 mAh.g(-1) at 200 mA g(-1), and after 100 cycles, the discharge capacity still remains at 712 mAh.g(-1), which is higher than those of the cells assembled with Al2O3/PVDF-coated separator and routine separator. (C) 2018 Elsevier B.V. All rights reserved.
机译：已制备具有LINO3 / AL2O3 / PVDF涂层的改性隔膜以保护锂阳极并增强锂 - 硫（LI-S）电池的循环性能。 直接与锂接触的功能涂层，并且在Al 2 O 3纳米颗粒中吸收的LINO3缓慢释放，为锂提供耐用的保护。 用LiNO3 / Al 2 O 3 / PVDF涂覆的分离器组装的电池的初始放电容量为1283mAh.g（-1），在200mA g（-1），在100次循环后，放电容量仍保持在712mah。 G（-1）高于用Al 2 O 3 / PVDF涂覆的分离器和常规分离器组装的细胞的G（1）。 （c）2018年elestvier b.v.保留所有权利。