High saturation magnetic flux density (B-s) nanocrystalline alloys are increasingly attractive due to their unique microstructure and outstanding magnetic performance. In this work, we report that the substitution of B for P essentially improves the B-s of FePBCCu amorphous alloys. Based on high B-s amorphous matrix, the Fe83.2P8B2C6Cu0.8 nanocrystalline alloy with high B-s of 1.77 T, low coercivity of 3.6 A/m and high effective permeability of 20,600 was developed. Such magnetic performance of Fe83.2P8B2C6Cu0.8 nanocrystalline alloy is closely associated with the uniform refined composite microstructure, where the alpha-Fe nanocrystals with high volume fraction, small size and high number density (similar to 1.8 x 10(23) m (-3)) were formed. This finding makes the FePBCCu composite a kind of promising soft-magnetic material in electrical and electronic fields.
机译：由于其独特的微观结构和出色的磁性性能，高饱和磁通密度（B-S）纳米晶合金越来越有吸引力。 在这项工作中，我们报告称B的替代为P基本上改善了Fepbccu非晶合金的B-S。 基于高B-S非晶基质，Fe83.2P8B2C6Cu0.8纳米晶合金具有高B-S的1.77吨，低矫顽力为3.6A / m，开发了20,600的高效率渗透率。 这种Fe83.2P8B2C6CU0.8纳米晶合金的这种磁性性能与均匀的精制复合微观结构密切相关，其中α-Fe纳米晶体具有高体积分数，小尺寸和高数密度（类似于1.8×10（23）M（ - 3））形成。 这一发现使FEPBCCU复合材料在电气和电子领域中有一种有前途的软磁材料。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号