Study of lithium ion conducting glasses with Li2SO4 addition

机译：用Li2SO4加入锂离子导电玻璃的研究

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Glasses of series 40Li(2)O: (40 - x)B2O3: 20SiO(2): xLi(2)SO(4) have been synthesized. The T-g, density, ionic conductivity, ionic transference number and FTIR of these glasses were studied. It was observed that with Li2SO4 addition, the T-g and density of these glasses decreased, while the ionic conductivity increased. There is a good correlation among T-g , density and electrical conductivity results. Ionic transference number suggest that glass samples studied in the present work are predominantly ion conducting in nature. The FTIR results also support the observed results of ionic conductivity with Li2SO4 addition. Among the glass samples studied, the maximum conductivity of 1.46 x 10(-2) S/cm at 523 K is exhibited by the glass sample 40Li(2)O: 32.5B(2)O(3): 20SiO(2): 7.5Li(2)SO(4). This glass composition has the potential for being used as a solid electrolyte.
机译：40Li（2）O：（40 - x）B2O3：20sio（2）：XLI（4）所以（4）已被合成。 研究了这些玻璃的T-G，密度，离子电导率，离子转移数和FTIR。 观察到，通过Li2SO 4加入，这些玻璃的T-G和密度降低，而离子电导率增加。 T-G，密度和电导率结果存在良好的相关性。 离子转移号表明本作研究中研究的玻璃样品主要是离子导电。 FTIR结果还支持与Li2SO4加入的观察结果的离子电导率结果。 在所研究的玻璃样品中，通过玻璃样品40Li（2）O：32.5b（2）O（3）：20sio（2）：32.5b（2）o（3）：32.5b（2）：3）：20sio（2）：3.46×10（2）o：32.5b（2）： 7.5li（2）所以（4）。 该玻璃组合物具有用作固体电解质的可能性。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号