首页> 外文期刊>Acta biomaterialia >Ca-Mg-Zn bulk metallic glasses as bioresorbable metals
【24h】

Ca-Mg-Zn bulk metallic glasses as bioresorbable metals

机译：Ca-Mg-Zn块状金属玻璃作为生物可吸收金属

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

A series of six unique Ca-based bulk metallic glasses were synthesized and characterized. The glasses were designed to consist solely of the biocompatible elements Ca, Mg and Zn, with the view to their potential use as bioresorbable metals for orthopaedic applications. The alloys had a critical casting thickness of up to 4.5 mm. Mechanical and thermophysical testing revealed a Youngs modulus (stiffness) of ～40 GPa. Glass transition temperatures ranged from 119 to 129 °C, above which the alloys can be formed like a thermoplastic polymer. In vitro biocorrosion testing using a combination of polarization and mass loss techniques revealed that the corrosion rate of these alloys is relatively rapid, although, in some cases, it may be tailored through alloy composition.
机译：合成并表征了一系列六种独特的Ca基块状金属玻璃。该玻璃被设计为仅由生物相容性元素Ca，Mg和Zn组成，以期将其潜在地用作骨科应用的生物可吸收金属。合金的临界铸造厚度最大为4.5毫米。机械和热物理测试表明，杨氏模量（刚度）约为40 GPa。玻璃化转变温度为119至129°C，在该温度以上，合金可以像热塑性聚合物一样形成。使用极化和质量损失技术的组合进行的体外生物腐蚀测试表明，尽管某些情况下可以通过合金成分来调整腐蚀速度，但这些合金的腐蚀速度相对较快。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号