Three kinds of Bi-Se nanocrystals (Bi2Se3, Bi8Se9 and Bi1.007Se0.993) have been synthesized via a hot-injection approach. The colloid morphology, from hexagonal to octahedron, strongly depends on the injection temperature. The growth mechanism of Bi-Se nanocrystals is revealed here. A higher temperature could cause the reduction reaction from Bi3+ to Bi, and accelerate the reaction speed of Bi-Se, thus causing a difference of monomer concentration in bulk solution, which impacts the shapes of bismuth selenide nanocrystals as well as the composition. The three Bi-Se nanocrystals also show different optical and photoelectrocatalyst performance.
机译：通过热注射方法合成了三种Bi-SE纳米晶（Bi2Se3，Bi8Se9和Bi1.007Se0.993）。 从六边形到八面体的胶体形态强烈取决于注射温度。 这里揭示了Bi-Se纳米晶体的生长机制。 较高的温度可能导致Bi3 +至Bi的还原反应，并加速Bi-Se的反应速度，从而引起本体溶液中单体浓度的差异，这会影响硒化烷烃纳米晶体的形状以及组合物。 三个Bi-SE纳米晶体还显示出不同的光学和光电催化剂性能。

著录项

  • 来源
    《RSC Advances》 |2016年第53期|共4页
  • 作者

    Jiang Yan; Hao Mengmeng; Jiang Liangxing; Liu Fangyang; Liu Yexiang;

  • 作者单位

    Cent S Univ Sch Met &

    Environm Changsha 410083 Peoples R China;

    Cent S Univ Sch Met &

    Environm Changsha 410083 Peoples R China;

    Cent S Univ Sch Met &

    Environm Changsha 410083 Peoples R China;

    Cent S Univ Sch Met &

    Environm Changsha 410083 Peoples R China;

    Cent S Univ Sch Met &

    Environm Changsha 410083 Peoples R China;

  • 收录信息
  • 原文格式 PDF
  • 正文语种 eng
  • 中图分类 化学;
  • 关键词

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号