Surface modification of polymers with bis(arylcarbene)s from bis(aryldiazomethane)s: preparation, dyeing and characterization

机译：来自双（Aryldiazomethane）S的双（芳基氨基甲酸酯）S的聚合物的表面改性：制备，染色和表征

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Modification of polymer beads by bis(arylcarbene) insertion provides access to materials with similar bulk properties, but different surface chemical characteristics, compared to the unmodified polymer. A subsequent dyeing process using different diazonium salts generates colored polymers with a variety of surface functional groups. XPS and solid state NMR spectra were used to characterize modified and dyed polymers, which showed this protocol was both successful and general. BET data showed that the surface area changed significantly after modification, while BJH data showed pore size distribution was unchanged. TG/DSC analysis and Elemental Analysis were also used to characterize modified polymers. This permitted calculation and comparison of the loadings of surface area and the modification effects with different chemical structure of bis(arylcarbene)s. This work shows that the bis(arylcarbene) system is as effective as mono(arylcarbene)s, but of significance since the starting bis(aryldiazomethane) s are more easily accessible and easier to handle than the mono(aryldiazomethane)s. All this data indicates that the surface property of polymers is modified.
机译：与未改性的聚合物相比，通过双（芳基甲醛）插入的聚合物珠子的改性提供了对具有相似堆积性质的材料，但不同的表面化学特性。使用不同重氮盐的随后的染色方法产生具有多种表面官能团的着色聚合物。 XPS和固态NMR光谱用于表征改性和染色聚合物，其显示该方案既成功又一般。 BET数据显示修改后表面积显着变化，而BJH数据显示孔径分布不变。 TG / DSC分析和元素分析还用于表征改性聚合物。这种允许的表面积载荷和与双（芳基甲苯）的不同化学结构的载荷和改性效应的计算和比较。这项工作表明，双（芳基甲苯）系统与单体（芳基比甲烷）S一样有效，但由于起始双（阿里德二氮胺甲烷）S更容易进入并且更容易处理而不是单可以（芳基二甲烷）S.所有这些数据表明聚合物的表面特性被修改。

著录项

  • 来源
    《RSC Advances》 |2016年第112期|共15页
  • 作者

    Yang Pengfei; Moloney Mark G.;

  • 作者单位

    Univ Oxford Dept Chem Chem Res Lab Oxford OX1 3TA England;

    Univ Oxford Dept Chem Chem Res Lab Oxford OX1 3TA England;

  • 收录信息
  • 原文格式 PDF
  • 正文语种 eng
  • 中图分类 化学;
  • 关键词

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号