首页> 外文期刊>RSC Advances >One-pot synthesis of long twin gold nanorods in a gelled surfactant solution
【24h】

One-pot synthesis of long twin gold nanorods in a gelled surfactant solution

机译：凝胶表面活性剂溶液中长双金纳米棒的单壶合成

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

A new one-pot synthesis method was developed for producing long twin gold nanorods with lengths of ca. 1755 nm, which have the potential to be arranged on a substrate using anisotropic surface modification. This method was achieved by using citrate-stabilized seeds in a gelled surfactant solution, i.e., in the mixture of hexadecyltrimethylammonium bromide and octadecyltrimethylammonium bromide at low temperature (20 degrees C). The yield (ca. 60%) of this method is relatively high. The mechanism of the present growth conditions was compared with those reported in previous studies. As expected, NO3 had an influence on the length of the gold nanorods and the longest ones were obtained at an optimal concentration of NO3, even for growth in the gelled surfactant solution. In contrast, the number of seeds in the growth solution had no effect on the lengths of the nanorod grown in the gelled surfactant.
机译：开发了一种新的单罐合成方法，用于制造具有长度的CA长度的长双胞胎金纳米棒。 1755nm，具有使用各向异性表面改性的底物布置在基材上。 通过在低温（20℃）的凝胶化表面活性剂溶液中使用凝胶化表面活性剂溶液中的柠檬酸盐稳定的种子，即在十六烷基三甲基溴化铵和八烷基三甲基溴化铵的混合物中实现该方法。 该方法的产量（约60％）相对较高。 将目前生长条件的机制与先前研究报告的那些进行比较。 正如预期的那样，NO3对金纳米棒的长度有影响，即使在凝胶化的表面活性剂溶液中的生长也是最佳NO 3的最佳浓度。 相反，生长溶液中的种子的数量对凝胶表面活性剂中生长的纳米棒的长度没有影响。

著录项

  • 来源
    《RSC Advances》 |2015年第44期|共6页
  • 作者

    Takenaka Y.;

  • 作者单位

    Natl Inst Adv Ind Sci &

    Technol Nanosyst Res Inst Tsukuba Ibaraki 3058565 Japan;

  • 收录信息
  • 原文格式 PDF
  • 正文语种 eng
  • 中图分类 化学;
  • 关键词

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号