首页> 外文期刊>Acta Crystallographica, Section B. Structural Science >Site occupancy and lattice parameters in sigma-phase Co-Cr alloys
【24h】

Site occupancy and lattice parameters in sigma-phase Co-Cr alloys

机译：σ相Co-Cr合金的位点占有率和晶格参数

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Neutron powder diffraction was used to study the distribution of Co and Cr atoms over different lattice sites as well as the lattice parameters of sigma-phase compounds Co100-x Cr x with x = 57.0, 62.7 and 65.8. From the diffractograms recorded in the temperature range of 4.2-300 K it was found for the five crystallographically independent sites that A (2a) and D (8i) are predominantly occupied by Co atoms, while sites B (4f), C (8i) and E (8j) mainly accommodate Cr atoms. The lattice parameters a and c exhibit linear temperature dependencies, with different expansion coefficients in the temperature ranges of 4.2-100 and 100-300 K.
机译：用中子粉末衍射法研究了Co和Cr原子在不同晶格位点上的分布，以及x = 57.0、62.7和65.8的σ相化合物Co100-x Cr x的晶格参数。从在4.2-300 K的温度范围内记录的衍射图可发现，在五个晶体学上独立的位点，A（2a）和D（8i）主要被Co原子占据，而位点B（4f），C（8i） E（8j）主要含有Cr原子。晶格参数a和c表现出线性温度依赖性，在4.2-100和100-300 K的温度范围内具有不同的膨胀系数。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号