首页> 外文期刊>Acta biomaterialia >Chemico-physical characterization of gelatin films modified with oxidized alginate.
【24h】

Chemico-physical characterization of gelatin films modified with oxidized alginate.

机译：氧化藻酸盐改性明胶薄膜的化学物理特征。

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The possibility of using low concentrations of dialdehyde alginate (ADA) to crosslink and stabilize gelatin films was investigated. The films were prepared from gelatin solutions at different concentrations (5, 10 and 15wt.%) containing different amounts of oxidized alginate (0, 1 and 3wt.% with respect to the weight of gelatin). The extent of crosslinking increases as a function of ADA concentration, up to about 23%. The presence of oxidized alginate provokes a significant reduction in the degree of swelling and of gelatin release in phosphate-buffered saline solution, enhancing the effect of gelatin concentration. Furthermore, the values of the Young's modulus, E, and of the stress at break, sigma(b), increase with increasing ADA concentration. The observed small, but appreciable, increase in thermal stability found by differential scanning calorimetric investigation is supported by X-ray diffraction results.
机译：研究了使用低浓度的二醛藻酸盐（ADA）来交联并稳定明胶薄膜的可能性。 薄膜由不同浓度（5,10和15wt％）的明胶溶液制备，含有不同量的氧化藻酸盐（0,1和3wt。相对于明胶的重量）。 交联的程度随着ADA浓度的函数而增加，高达约23％。 氧化藻酸盐的存在引起磷酸盐缓冲盐水溶液中肿胀和明胶释放的显着降低，增强了明胶浓度的影响。 此外，杨氏模量，E和断裂应力的值，Sigma（B），随着ADA浓度的增加而增加。 通过差分扫描量热调查发现的X射线衍射结果支持的小，但也可观地增加热稳定性的增加。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号