摘要

For spinal-fixation applications, implants should have a high Young's modulus to reduce springback during operations, though a low Young's modulus is required to prevent stress shielding for patients after surgeries. In the present study, Ti-29Nb-13Ta-4.6Zr alloy (TNTZ) with a low Young's modulus was modified by adding Cr to obtain a higher deformation-induced Young's modulus in order to satisfy these contradictory requirements. Two newly designed alloys, TNTZ-8Ti-2Cr and TNTZ-16Ti-4Cr, possess more stable β phases than TNTZ. These alloys consist of single β phases and exhibit relatively low Young's moduli of <65GPa after solution treatment. However, after cold rolling, they exhibit higher Young's moduli owing to a deformation-induced ω-phase transformation. These modified TNTZ alloys show significantly less springback than the original TNTZ alloy based on tensile and bending loading-unloading tests. Thus, the Cr-added TNTZ alloys are beneficial for spinal-fixation applications.
机译：对于脊柱固定应用，植入物应具有高杨氏模量，以减少运营期间的回弹，但需要低杨氏模量来防止手术后患者的应力屏蔽。 在本研究中，通过添加CR来改变具有低杨氏模量的Ti-29NB-13TA-4.6ZR合金（TNTZ）以获得更高的变形诱导的杨氏模量，以满足这些矛盾的要求。 两个新设计的合金，TNTZ-8TI-2CR和TNTZ-16TI-4CR，比TNTZ更稳定的β相。 这些合金包括单β相，在溶液处理后表现出相对较低的杨氏Moduli。 然而，在冷轧之后，由于变形诱导的ω相变化，它们表现出更高的杨氏模。 这些改性TNTZ合金的回弹比原始TNTZ合金显着较低，基于拉伸和弯曲的装载卸载试验。 因此，CR添加的TNTZ合金有利于脊柱固定应用。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号