首页> 外文期刊>Crystal growth & design >LiNaB4O7 crystals as a material for optically induced elastoopticity
【24h】

LiNaB4O7 crystals as a material for optically induced elastoopticity

机译：LiNaB4O7晶体作为光学诱导弹塑性的材料

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

During bicolor optical treatment by Nd: YAG laser radiation (lambda = 1060 nm) and its coherent second harmonic (lambda = 530 nm) of the LiNaB4O7 (LNTB) crystals ( space group Fdd2), a substantial increase in the elastooptic coefficient at lambda = 633 nm (up to 9 x 10(-13) m(2)/N) was revealed. The corresponding effect was maximal for the diagonal piezooptic POxxxx tensor component, where x is directed along the second-order crystallographic axes. The effect appears at temperatures below 80 K and achieves its maximal value at T = 4.2 K. The phenomenon appears after 2 min of optical treatment under laser power densities above 0.6 GW/cm(2) and is saturated after 5 min of the bicolor optical coherent treatment. The elastooptical effect decreases at least one order at temperatures below 50 K and 6 min after switching off the bicolor laser treatment.
机译：在Nd：YAG激光辐射（λ= 1060 nm）及其相关的LiNaB4O7（LNTB）晶体（空间群Fdd2）的二次谐波（λ= 530 nm）进行双色光学处理期间，λ=时的弹性系数大大增加揭示了633 nm（最高达9 x 10（-13）m（2）/ N）。对于对角压电POxxxx张量分量，相应的影响最大，其中x沿二阶晶体学轴指向。该效应出现在低于80 K的温度下，并在T = 4.2 K时达到最大值。该现象在激光功率密度超过0.6 GW / cm（2）的光学处理2分钟后出现，并在5分钟的双色光学区域达到饱和。相干治疗。在关闭双色激光处理后，在低于50 K的温度和6分钟的温度下，弹性效应至少降低一个阶。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号