首页> 外文期刊>Crystallography reports >Neutron Diffraction Study of the Phase Transformations in Titanium Carbohydride TiC0.50Hy
【24h】

Neutron Diffraction Study of the Phase Transformations in Titanium Carbohydride TiC0.50Hy

机译：中子衍射研究碳氢化钛的相变性Tic0.50HY

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

It is shown that the ordered phase of titanium carbohydride TiC0.50H0.31 with a face-centered cubic lattice (sp. gr. Fdm), obtained by self-propagating high-temperature synthesis, has an ordered antiphase domain structure with a period P = 16. This period is much larger than that in TiC0.50Hy (y 0.22), with a lower hydrogen content (P approximate to 11). It is shown that TiC0.50H0.31 decomposes at temperatures T 900 degrees C into the cubic phase of titanium carbide TiCx (x 0.70) (sp. gr. Fmm) and the trigonal phase of titanium carbohydride Ti2CvHz (sp. gr. Pm1).
机译：结果表明，通过自我繁殖的高温合成获得的面为中心的立方晶格（SP.CR.CM）的钛碳水化合物Tic0.30.31的有序相。 = 16.该时期比Tic0.50hy（y 0.22）中的时间大得多，氢含量较低（P近似为11）。 结果表明，Tic0.50H0.31在温度T 900℃下分解成碳化钛TiCx（×0.70）（SP.CR.FMM）和钛碳水化合物Ti2CVHz的三角形相（SP.GM1） 。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号