ID natiostructures of Zn1-xCoxO (x = 0, 0.03 and 0.05) and Co and Li codoped ZnO (Zn0.85Li0.10Co0.05O) were prepared by a soft chemical method. We report a very interesting observation of morphological control and transformation of ZnO nanorods to spherical particles induced by Co substitution. It is also remarkable to note that the morphology completely reverts back to rod shape by Li incorporation. In addition to this unusual observation, the Li incorporation enhances the room-temperature ferromagnetic (RTFM) properties. These experimental observations are well-supported by theory work as well. These results are significant, as the I D RTFM will have implications in spintronic devices.
机译：通过软化学方法制备了Zn1-xCoxO（x = 0、0.03和0.05）以及Co和Li共掺杂的ZnO（Zn0.85Li0.10Co0.05O）的ID结构。我们报告了非常有趣的观察到的形态控制和ZnO纳米棒向Co取代诱导的球形颗粒转化的观察。还值得注意的是，通过掺入Li，该形态完全恢复为棒状。除了这种不寻常的观察结果之外，Li的掺入还增强了室温铁磁（RTFM）性能。这些实验观察也得到理论工作的充分支持。这些结果非常重要，因为I RTFM将对自旋电子器件产生影响。