On the electrochemical behaviour of V-N-8Cr weathering steel in simulated industrial atmosphere

机译：关于模拟工业大气中V-N-8CR风化钢的电化学行为

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

We have studied here the wet/dry cyclic corrosion behaviour of V-N-0.8Cr weathering steel and compared with a reference steel (Q345B) in 0.01 mol/L NaHSO3 simulated industrial atmosphere. The study indicated that the coherent protective oxide layer formed in the surface of V-N-0.8Cr microalloyed weathering steel, contained corrosion resistant alloying elements (Cr, Ni, Cu, P, Mo). The addition of Cr significantly inhibited the corrosion of weathering steel. The corrosion rate of V-N-0.8Cr and Q345B steel after 360 h corrosion were 1.60 g/(h center dot cm(2)) and 2.42 g/(h center dot cm(2)) respectively. The major corrosion products in both the steels mainly constituted of alpha-FeOOH and gamma- FeOOH and Fe3O4. The stratification of the corrosion layer evolved into a dual-layer structure, where the outer layer was dense and the inner layer was a loose and porous structure in V-N-0.8Cr weathering steel. This is different from previous studies. Cr tends to be concentrated in the inner corrosion layer.
机译：我们在此研究了V-N-0.8CR风化钢的湿/干循环腐蚀行为，并与0.01mol / L NaHSO3的参考钢（Q345B）进行了比较。该研究表明，在V-N-0.8CR微合金化钢的表面形成的相干保护氧化物层，含有耐腐蚀合金元素（Cr，Ni，Cu，P，Mo）。添加CR显着抑制了耐候钢的腐蚀。 360小时腐蚀后V-N-0.8Cr和Q345b钢的腐蚀速率分别为1.60g /（h中心点Cm（2））和2.42g /（h中心点Cm（2））。两种钢中的主要腐蚀产品主要由Alpha-FeOh和Gamma-FeOh和Fe3O4构成。腐蚀层的分层进化成双层结构，其中外层是致密的，内层是V-N-0.8CR风化钢中的松散和多孔结构。这与以往的研究不同。 CR倾向于集中在内腐蚀层中。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号