首页> 外文期刊>Crystal growth & design >Epitaxial growth of NaGd_(0.935)Yb_(0.065)(WO _4)_2 layers on lattice matched tetragonal double tungstate substrates for ultrafast thin disk lasers
【24h】

Epitaxial growth of NaGd_(0.935)Yb_(0.065)(WO _4)_2 layers on lattice matched tetragonal double tungstate substrates for ultrafast thin disk lasers

机译：NaGd_（0.935）Yb_（0.065）（WO _4）_2层在晶格匹配的四方双钨酸盐衬底上的外延生长，用于超快薄盘激光器

获取原文
获取原文并翻译 | 示例
   

获取外文期刊封面封底 >>

       
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Liquid-phase epitaxial growth of Yb~(3+) doped NaGd(WO _4)_2 crystalline layers has been obtained on Y modified NaGd(WO_4)_2 Czochralski grown single crystal substrates. It is shown that the lattice parameter of the layer and substrate can be equalized by proper selection of the Yb and Y compositions. The epitaxial layers obtained are highly transparent, with thicknesses in the range 10-70 μm, and with crystallographic quality close to that of the used substrates. The spectroscopic properties of Yb~(3+) in the layer are anisotropic and similar to those of Yb-doped NaGd(WO_4)_2 single crystals. The layers are envisaged as optical gain media for the design of ultrafast modelocked thin disk lasers.
机译：在Y修饰的NaGd（WO_4）_2直拉生长的单晶衬底上获得了Yb〜（3+）掺杂的NaGd（WO_4）_2晶体层的液相外延生长。结果表明，通过适当选择Yb和Y成分，可以使层和衬底的晶格参数相等。所获得的外延层是高度透明的，厚度在10-70μm的范围内，并且晶体学质量接近于所用基板的晶体学质量。该层中Yb〜（3+）的光谱性质是各向异性的，并且类似于掺Yb的NaGd（WO_4）_2单晶。可以将这些层用作光学增益介质，以设计超快锁模薄盘激光器。