首页> 外文期刊>ACS Sustainable Chemistry & Engineering >Structural, Dielectric, and Thermal Properties of Pb Free Molybdate Based Ultralow Temperature Glass
【24h】

Structural, Dielectric, and Thermal Properties of Pb Free Molybdate Based Ultralow Temperature Glass

机译：无铅钼酸盐基超低温玻璃的结构，介电和热性能

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

A new glass with ultralow glass transition temperature based on 10Li2O-10Na2O-20K2O-60MoO3 (LNKM) has been developed by conventional glass melting and quenching process. The glass has ultralow glass transition and melting temperatures being 198 and 350 °C respectively. The glass exhibits a coefficient of thermal expansion of 17 ppm/°C in the temperature range of 25-300 °C. Xray diffraction and Raman spectroscopic studies indicate that the glass is partially crystallized. The chemical and elemental composition of the glass is confirmed by X-ray photoelectron spectroscopy. The glass pellet heat treated at 300 °C has a relative permittivity of 5.07 and dielectric loss tangent of 0.006 at 1 MHz. At 9.97 GHz, it shows a relative permittivity of 4.85 and dielectric loss tangent of 0.0009. The temperature dependence of the relative permittivity at 1 MHz and 9.97 GHz of the glass is 307 ppm/°C (temperature range 20- 100 °C) and 291 ppm/°C (temperature range 25-85 °C), respectively.
机译：通过传统的玻璃熔化和淬火工艺，开发了一种基于10Li2O-10Na2O-20K2O-60MoO3（LNKM）的超低玻璃化转变温度的玻璃。该玻璃具有极低的玻璃化转变温度，熔融温度分别为198和350°C。在25-300°C的温度范围内，玻璃的热膨胀系数为17 ppm /°C。 X射线衍射和拉曼光谱研究表明玻璃是部分结晶的。玻璃的化学和元素组成通过X射线光电子能谱确认。在300 MHz下进行热处理的玻璃颗粒在1 MHz下的相对介电常数为5.07，介电损耗角正切为0.006。在9.97 GHz处，它的相对介电常数为4.85，介电损耗角正切为0.0009。玻璃在1 MHz和9.97 GHz时的相对介电常数对温度的依赖性分别为307 ppm /°C（温度范围20-100°C）和291 ppm /°C（温度范围25-85°C）。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号