首页> 外文期刊>Materials and Corrosion >Corrosion initiation of Hastelloy C-2000 in an HCl-polluted atmosphere
【24h】

Corrosion initiation of Hastelloy C-2000 in an HCl-polluted atmosphere

机译：HCL污染的气氛中Hastelloy C-2000的腐蚀引发

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

In this study, welded and non-welded Hastelloy C-2000 samples are tested at room temperature in HCl environments, with two experiments: one in hydrochloric acid solutions and one in HCl vapor/condensate phases. In the hydrochloric acid solutions, there is no corrosion after more than 900 hr of exposure. In the humid air polluted by HCl, corrosion occurs in the form of an intergranular attack at the metal grain boundaries. In the weld bead zone, areas rich in molybdenum and depleted of nickel seem to be less susceptible to corrosion than the zones depleted of molybdenum and rich in nickel. This study highlights that Hastelloy C-2000, exposed to HCl vapor/condensate phases, is more penalizing than when immersed in an HCl solution, which is due to the presence of oxygen.
机译：在本研究中，在HCl环境中在室温下测试焊接和非焊接的HASTELLOY C-2000样品，两次实验：一种在盐酸溶液中，一种在HCL蒸气/冷凝水中。 在盐酸溶液中，超过900小时的暴露后没有腐蚀。 在通过HCl污染的潮湿空气中，腐蚀以金属晶界的晶体攻击的形式发生。 在焊珠区中，富含钼和镍耗尽的区域似乎不太易受腐蚀的腐蚀，而不是钼和富含镍的区域。 本研究突出了暴露于HCl蒸气/缩合阶段的Hastelloy C-2000，比浸入HCl溶液中的抗生素，这是由于氧的存在。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号