首页> 外文期刊>Crystallography reports >Growth from gas cavities in a molten salt and properties of superconducting Bi2Sr2CaCu2O8+delta single crystals
【24h】

Growth from gas cavities in a molten salt and properties of superconducting Bi2Sr2CaCu2O8+delta single crystals

机译：熔融盐中气体腔的生长和Bi2Sr2CaCu2O8 +δ超导单晶的性质

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Perfect single crystals of the high-temperature superconductor Bi2Sr2CaCu2O8+delta with the super-conducting, transition temperature T-C = 72-85 K (depending on the crystallization conditions) are obtained by the method of free growth in gas cavities formed in a KCl solution-melt. The specific features of the growth process are in the formation of an enclosed growth gas cavity in a (previously synthesized) blend of a specified phase composition dissolved in KCl and the free crystal growth in this cavity. The combination of growth and high-temperature annealing in the same process made it possible to obtain uniform (DeltaT(C) = 1.5 K) single crystals with stable superconducting properties. Annealing of the grown single crystals in oxygen or in air in the temperature range 400-850degreesC confirmed that the crystals with maximum values of TC are optimally doped. (C) 2005 Pleiades Publishing, Inc.
机译：通过在KCl溶液中形成的气体腔中自由生长的方法获得具有超导转变温度TC = 72-85 K（取决于结晶条件）的高温超导体Bi2Sr2CaCu2O8 +δ的完美单晶。熔化。生长过程的特定特征是在（先前合成的）混合物中形成了一个封闭的生长气体腔，该混合物由溶解在KCl中的特定相组成和在该腔中的自由晶体生长组成。通过在同一过程中进行生长和高温退火相结合，可以获得具有稳定超导特性的均匀（DeltaT（C）= 1.5 K）单晶。在氧气或空气中在400-850摄氏度的温度范围内对生长的单晶进行退火，证实了具有TC最大值的晶体得到了最佳掺杂。 （C）2005年Pleiades Publishing，Inc.