首页> 外文期刊>Crystal Research and Technology: Journal of Experimental and Industrial Crystallography >Growth and characterization of L-prolinium tartrate - A new organic NLO material
【24h】

Growth and characterization of L-prolinium tartrate - A new organic NLO material

机译：酒石酸L-脯氨酸lin的生长与表征-一种新型的NLO有机材料

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Single crystals of L-Prolinium tartrate (C5H10NO2)(+) (C4H5O6)(-), a new organic non-linear optical material of size: 15 x 10 x 10 mm(3) were grown using submerged seed solution growth method. Characterization of the crystals was made using single crystal X-ray diffraction and density determination. Spectroscopic, thermal, optical and mechanical studies were carried out. These studies show that the crystals are thermally stable upto 161 degrees C, transparent for the fundamental and second harmonic generation of Nd: YAG (lambda = 1064 nm) laser and possess good mechanical strength. Second harmonic generation (SHG) conversion efficiency was investigated to explore the NLO characteristics of this material using Kurtz and Perry method and it was found that the SHG conversion efficiency is about 90% of that of the standard KDP crystals. Laser damage threshold study was also carried out. (C) 2007 WILE-VCH Verlag GmbH & Co. KGaA, Weinheim.
机译：酒石酸L-脯氨酸（C5H10NO2）（+）（C4H5O6）（-）的单晶是采用浸没种子溶液生长法生长的新型有机非线性光学材料，尺寸为15 x 10 x 10 mm（3）。使用单晶X射线衍射和密度测定法对晶体进行表征。进行了光谱，热，光学和机械研究。这些研究表明，该晶体在高达161摄氏度的温度下都是热稳定的，对于Nd：YAG（λ= 1064 nm）激光的基波和二次谐波生成透明，并且具有良好的机械强度。使用Kurtz和Perry方法研究了二次谐波（SHG）转换效率，以探索该材料的NLO特性，发现SHG转换效率约为标准KDP晶体的90％。还进行了激光损伤阈值研究。 （C）2007 WILE-VCH Verlag GmbH＆Co.KGaA，Weinheim。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号