首页> 外文期刊>Surface review and letters >TEXTURE AND STRUCTURE VARIATION OF PEROVSKITE LaFeO3/ZSM-5 DURING HIGH-TEMPERATURE DESULFURIZATION
【24h】

TEXTURE AND STRUCTURE VARIATION OF PEROVSKITE LaFeO3/ZSM-5 DURING HIGH-TEMPERATURE DESULFURIZATION

机译：高温脱硫期间Perovskite Lafeo3 / ZSM-5的纹理和结构变化

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Perovskite LaFeO3/ZSM-5 is synthesized via citrate route for H2S removal at high temperatures. It shows good thermal stability after heat treatment at 500-700 degrees C with respect to slight changes in crystallographic phase and textural property. It presents the optimal desulfurization performance at 600 degrees C with sulfur capacity of 1017 mu molS/g and products of S, LaS2, and Fe7S8. Sulfidation at 500 degrees C yields the same products as sulfidation at 600 degrees C but displays the lowest sulfur capacity of 408 mu molS/g. Sulfidation at 700 degrees C produces La2O2S, Fe3S4, and unreacted LaFeO3. The activation energy of the sulfidation reaction over LaFeO3/ZSM-5 is 109.6 kJ/mol.
机译：通过在高温下的H2S去除的柠檬酸盐合成钙钛矿LafeO3 / ZSM-5。 它在500-700摄氏度的热处理后显示出良好的热稳定性，相对于晶体相位和纹理性质的微小变化。 它以600摄氏度为600℃的最佳脱硫性能，硫容量为1017μmol/ g和S，LAS2和FE7S8的产品。 500℃的硫化产生与600摄氏度的硫化相同的产品，但显示器为408μmmols/ g的最低硫容量。 700摄氏度的硫化产生La2O2s，Fe3S4和未反应的Lafeo3。 通过LafeO3 / ZSM-5对硫化反应的活化能量为109.6kJ / mol。