Preventing or accelerating galvanic corrosion through the application of a proper external magnetic field

机译：通过施加适当的外部磁场来防止或加速电偶腐蚀

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The effect of an external magnetic field on the corrosion behaviour of a galvanic couple, zinc (Zn)-stainless steel (SS 316L), has been investigated in a 0.055 mol L~(-1) potassium chloride (KCl) solution. The impact of the orientation as well as the magnetic flux density B (Wb m~(-2)) on the corrosion progression of the galvanic couple, is evaluated heuristically by monitoring the corrosion potential E_(corr) (mV) and the current density I_(corr) (μA cm~(-2)) of the system. A strong influence of the magnitude and orientation of the magnetic field on the Zn-SS316L galvanic couple corrosion was observed, whereas the field was proven to act either protective or accelerating in terms of corrosion.
机译：在0.055 mol L〜（-1）氯化钾（KCl）溶液中，研究了外部磁场对电偶锌（Zn）-不锈钢（SS 316L）腐蚀行为的影响。通过监测腐蚀电位E_（corr）（mV）和电流密度，通过试探法评估了取向以及磁通密度B（Wb m〜（-2））对电偶腐蚀的影响系统的I_（corr）（μAcm〜（-2））。观察到磁场的大小和方向对Zn-SS316L电偶腐蚀有很大的影响，而事实证明该磁场在腐蚀方面起保护作用或加速作用。