Electrochemical synthesis of transition metal oxide nitrides with ε-TaN, δ-NbN and γ′-Mo2N structure type in a molten salt system

机译：熔盐体系中ε-TAN，δ-NBN和γ-MO2N结构型过渡金属氧化物氮化物的电化学合成

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The three nitrides ε-TaN, δ-NbN and γ′-Mo2N have been synthesized electrochemically from the elements at 450°C in a molten salt mixture LiCl/KCl:Li3N. For all compounds the working electrode consisting of a tantalum, niobium or molybdenum foil was anodically polarized and the system was fed with dry nitrogen. The applied constant voltage was 2.5 V (for ε-TaN), 2.2 V (for δ-NbN), and 2.8 V (for γ′-Mo2N). Chemical analysis on N and O resulted in compositions of TaN0.81(1)O0.13(2), NbN1.17(2)O0.28(1) and MoN0.88(1)O0.11(1), respectively. Lattice parameters of ε-TaN refined by the Rietveld method are a?=? 519.537(4) and c?=?291.021(3) pm. The other two nitrides crystallize in the cubic system (rocksalt type) with a?=?436.98(2) pm for δ-NbN and with a?=?417.25(2) pm for γ′-Mo2N.
机译：在熔融盐混合物LiCl / Kcl：Li3N中，从450℃的元素电化学中，在450℃下电化学地已经合成了三种氮ε-TAN，δ-NBN和γ-MO2N。 对于所有化合物，由钽，铌或钼箔组成的工作电极是阳极偏振的，并且用干燥的氮气进料。 施加的恒定电压为2.5V（对于ε-TAN），2.2V（对于δ-NBN）和2.8V（对于γ'-MO2N）。 N和O的化学分析得到Tan0.81（1）oO13（2），Nbn1.17（2）o0.28（1）和mon0.88（1）o0.11（1）的组合物。 。 RIETVELD方法精制的ε-TAN的晶格参数是a？=？ 519.537（4）和C？=？291.021（3）PM。 另外两个氮化物在立方体系统（RocksAlt型）中结晶，具有Δ-nbn的Δ= 436.98（2）pm，并且对于γ'-mo2n，pm = 417.25（2）pm。