首页> 外文期刊>JOM >Comparison of Natural and Nano-synthetically-Produced Hydroxyapatite Powder
【24h】

Comparison of Natural and Nano-synthetically-Produced Hydroxyapatite Powder

机译：天然和纳米合成羟基磷灰石粉的比较

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Hydroxyapatite (HAp) is a bioactive material that forms the main mineral part of teeth, hard tissues, and bone in humans. The goal of the present study is to prepare hydroxyapatite from bio-waste materials such as fish bone and bovine femur bone at different calcination temperatures, selecting the optimal calcination temperatures and then comparing these with commercial nano-HAp. The HAp was synthesized from the bio-waste materials by a calcination process in a thermal dry and fire furnace with different calcination temperatures, heating rates and cooling rates all carefully controlled. The best results were obtained at 950 degrees C since, at this temperature, the Ca/P ratio reached 1.6589 for fish bone and 1.7058 for bovine femur bone, which is close to the commercial stoichiometric nano-HAp ratio of 1.67.
机译：羟基磷灰石（HAP）是一种生物活性材料，形成牙齿，硬组织和人类骨骼的主要矿物部分。 本研究的目标是在不同煅烧温度下从生物废料等生物废物材料中制备羟基磷灰石，选择最佳煅烧温度，然后用商业纳米HAP进行比较。 通过具有不同煅烧温度，加热速率和冷却速率的煅烧过程，通过煅烧过程从生物废料中的煅烧过程合成，加热速度和冷却速率都精心控制。 在该温度下，在950℃下获得最佳结果，在该温度下，Ca / P比为Fish Bone达到1.6589，牛股骨骨骼为1.7058，其接近商业化学计量纳米Hap比率为1.67。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号