The inhibition effect of gum arabic (GA) was investigated using weight loss measurements and electrochemical techniques. The results show that the inhibition efficiency of GA increased with an increase in the concentration of the inhibitor but decreased with the temperature. Immersion time was found to have a profound effect on the corrosion inhibition performance of the inhibitor. Polarization measurements revealed that GA was a mixed-type inhibitor, with higher influence on the anodic reaction. The inhibitor followed the Temkin's adsorption isotherm, and the values of the standard free adsorption energy indicate a mixed-type adsorption, with the physical adsorption being more dominant. SEM-EDS and FT-IR measurements were also employed to support the findings.
机译：使用减肥测量和电化学技术研究了阿拉伯语（Ga）的抑制作用。 结果表明，Ga的抑制效率随着抑制剂浓度的增加而增加，但随着温度降低。 发现浸渍时间对抑制剂的腐蚀抑制性能产生深远的影响。 偏振测量显示Ga是混合型抑制剂，对阳极反应的影响较高。 抑制剂遵循Temkin的吸附等温线，标准游泳能量的值表明混合型吸附，物理吸附更大。 SEM-EDS和FT-IR测量也用于支持调查结果。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号