首页> 外文期刊>Journal of Materials Engineering and Performance >Effects of Nd Addition on the Microstructure and Mechanical Properties of Extruded Mg-6Gd-2.5Y-0.5Zr Alloy
【24h】

Effects of Nd Addition on the Microstructure and Mechanical Properties of Extruded Mg-6Gd-2.5Y-0.5Zr Alloy

机译：ND添加对挤出Mg-6GD-2.5Y-0.5亿合金微观结构和机械性能的影响

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The microstructure, age-hardening behavior, mechanical properties and texture of extruded Mg-6Gd-2.5Y-0.5Zr alloys with various additions of Nd have been investigated through optical microscopy, x-ray diffraction, scanning electron microscopy, transmission electron microscopy, electron back-scattered diffraction, hardness and tensile tests. The results indicate that the number of second-phase particles in the as-extruded alloys increases (especially with the addition of 1.5 wt.% Nd), and the amount of the strengthening beta' phase in the peak-aged sample initially increases, and then decreases when the content of Nd increases above 1.0 wt.%. The precipitation of second-phase particles in the extrusion process weakens the age strengthening. The peak-aged Mg-6Gd-2.5Y-1Nd-0.5Zr alloy shows a maximum yield strength of 259 MPa and an ultimate tensile strength of 350 MPa, which can be attributed to the finely dispersed strengthening beta' phase. All as-extruded alloys exhibit that (0001) planes are aligned perpendicular to the extrusion direction, and the maximum intensity of the texture increases gradually with Nd addition.
机译：通过光学显微镜，X射线衍射，扫描电子显微镜，透射电子显微镜，电子，通过光学显微镜，X射线衍射，扫描电子显微镜，电子显微镜，电子进行了微观结构背散射衍射，硬度和拉伸试验。结果表明，用挤出合金中的第二相颗粒的数量增加（特别是加入1.5重量％Nd），并且峰老化样品中的强化β相的量最初增加，并且然后在ND的含量增加到1.0重量％的情况下增加。％。挤出过程中的二相颗粒的沉淀削弱了年龄加强。峰值Mg-6GD-2.5Y-1ND-0.5ZR合金显示出259MPa的最大屈服强度和350MPa的最终拉伸强度，其可归因于细分的强化强化β相。所有作为挤出合金表现出（0001）平面垂直于挤出方向对齐，并且纹理的最大强度随ND添加而逐渐增加。