首页> 外文期刊>Journal Of The South African Institute Of Mining & Metallurgy >Production of metallurgical-grade silicon from Egyptian quartz
【24h】

Production of metallurgical-grade silicon from Egyptian quartz

机译：从埃及石英中生产冶金级硅

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Metallurgical-grade silicon (MG-Si) was successfully produced by carbothermic reduction-smelting of Egyptian quartz using a mixture of carbonaceous materials in a locally made semi-pilot submerged arc furnace. The effects of different technical parameters such as the carbon to silica ratio, smelting time, power input, and weight ratio of carbon sources were investigated. The MG-Si product was characterized by X-ray diffraction (XRD), X-ray fluorescence (XRF), and scanning electron microscopy (SEM). A maximum silicon recovery of about 75% at a product purity of about 97% was achieved under the optimum experimental conditions of 80 minutes' smelting time, 48 kW power input, and a carbon/silica ratio of 0.39.
机译：通过在局部制造的半导体浸没式电弧炉中使用碳质材料的混合物，通过碳水化的石英冶炼冶炼冶炼级硅（Mg-Si）成功生产。 研究了不同技术参数如碳与二氧化硅比，冶炼时间，功率输入和碳源的重量比的影响。 Mg-Si产物的特征在于X射线衍射（XRD），X射线荧光（XRF）和扫描电子显微镜（SEM）。 在80分钟熔炼时间，48 kW功率输入的最佳实验条件下，在最佳实验条件下实现了约97％的产物纯度的最大硅回收率约为97％，碳/二氧化硅比为0.39。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号