首页> 外文期刊>ACS applied materials & interfaces >Electrochemical Synthesis of Poly(3,4-ethylenedioxythiophene) Film Having Dot Structures for Diffraction Grating
【24h】

Electrochemical Synthesis of Poly(3,4-ethylenedioxythiophene) Film Having Dot Structures for Diffraction Grating

机译：具有用于衍射光栅的点结构的聚（3,4-亚乙二醇噻吩）膜的电化学合成

获取原文
获取原文并翻译 | 示例
   

获取外文期刊封面封底 >>

       
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Poly(3,4-ethylenedioxythiophene) (PEDOT) dot micro/nanostructures are synthesized by electrochemical polymerization in a concentrated hydroxypropyl cellulose (HPC) liquid crystal electrolyte solution. Surface observations by scanning electron microscopy and atomic force microscopy reveal micro/nanostructures having hemisphere-like dots on the surface of the PEDOT film, which causes light diffraction at ultraviolet and visible light wavelengths. The size of the dots depends on the concentration of the HPC electrolyte solution, decreasing with increasing the HPC concentration. Electrochemical oxidation and reduction causes changes in the color of the PEDOT film and the diffracted light. Moreover, Au coating on the surface of the PEDOT film enhances the diffracted light reflection intensity by more than tenfold compared to the noncoated PEDOT film.
机译：聚（3,4-亚乙二氧基噻吩）（PEDOT）点微/纳米结构通过浓羟丙基纤维素（HPC）液晶电解质溶液中的电化学聚合来合成。 通过扫描电子显微镜和原子力显微镜揭示在佩特膜表面上具有半球状点的微/纳米结构，这导致紫外线和可见光波长的光衍射。 点的尺寸取决于HPC电解质溶液的浓度，随着HPC浓度的增加而降低。 电化学氧化和还原导致佩特膜的颜色和衍射光的变化。 此外，与非涂层佩特膜相比，佩特膜表面上的Au涂层增强了多于十倍的衍射光反射强度。