首页> 外文期刊>Journal of Phase Equilibria and Diffusion >Experimental Investigation of the Ni-V-Zn Ternary System
【24h】

Experimental Investigation of the Ni-V-Zn Ternary System

机译：Ni-V-Zn三元系统的实验研究

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The 450 and 600 degrees C isothermal sections of the Ni-V-Zn ternary system have been investigated through Scanning Electron Microscopy (SEM), Energy Dispersive Spectroscopy (EDS) and x-ray Diffraction (XRD) technique. Eight three-phase regions have been confirmed at the 450 degrees C section and nine three-phase regions exist at the 600 degrees C one. Experimental results indicate that it is difficult for Ni to dissolve in VZn3 and V4Zn5. The solid solubilities of V in gamma(Ni2Zn11) and beta(1)(NiZn) are 1.4 and 3.7 at.% at 450 degrees C, respectively, while V in gamma and beta(1) are 2.5 and 4.0 at.% at 600 degrees C, respectively. The solid solubilities of Zn in Ni2V7, sigma(Ni2V3), Ni2V and Ni3V are 0.5, 4.7, 2.3 and 2.6 at.% at 450 degrees C as well as 0.5, 9.5, 2.2 and 2.8 at.% at 600 degrees C, respectively. No ternary compound has been found in this work.
机译：采用扫描电子显微镜（SEM）、能谱仪（EDS）和x射线衍射（XRD）技术研究了Ni-V-Zn三元系450℃和600℃等温截面。在450摄氏度的断面上已经确认了八个三相区，在600摄氏度的断面上存在九个三相区。实验结果表明，镍在VZn3和V4Zn5中很难溶解。V在γ（Ni2Zn11）和β（1）（NiZn）中的固溶度分别为1.4和3.7 at.%在450摄氏度时，γ和β（1）中的V分别为2.5%和4.0%分别在600摄氏度。Zn在Ni2V7、sigma（Ni2V3）、Ni2V和Ni3V中的固溶性分别为0.5、4.7、2.3和2.6 at.%在450摄氏度以及0.5、9.5、2.2和2.8摄氏度时分别在600摄氏度。在这项工作中没有发现三元化合物。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号