Nano-crystalline aluminum was synthesized by a new method of ball-milling technique from ingots of 99.8 wt. percent Al. The effect of pressure on the microstructure and mechanical properties of compacted ball-milled aluminum was investigated in a pressure range up to 300 Pa. The dislocation density and micro-hardness of our specimens increase by increasing the pressure. The best fit line describes the H-P relationship dependence of micro-hardness (H_v0.010) on the grain size for compacted aluminum obeys the following formula: H_v0.010 = 35.42~(-1/2)+245.02(kg mm~(-2)).
机译：通过球磨技术的新方法，从99.8 wt。％的铸锭合成了纳米晶铝。铝百分比在最高300 Pa的压力范围内，研究了压力对压实球磨铝的微观结构和力学性能的影响。压力的增加会增加样品的位错密度和显微硬度。最佳拟合线描述压实铝的HP微观硬度（H_v0.010）与晶粒尺寸的关系，其服从以下公式：H_v0.010 = 35.42D〜（-1/2）+245.02（kg mm 〜（-2））。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号