首页> 外文期刊>Fullerene science and technology >Synthesis of high-molecular-weight [60]fullerene pearl-necklace polyamides derived from equatorial-[60]fullerenobisacetic acid
【24h】

Synthesis of high-molecular-weight [60]fullerene pearl-necklace polyamides derived from equatorial-[60]fullerenobisacetic acid

机译：赤道-[60]富勒烯双乙酸衍生的高分子量[60]富勒烯珍珠项链聚酰胺的合成

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

A series of [60]fullerene pearl-necklace polyamides, consisting of equatorial[60]fullerenobisacetic acid and various chromophoric aromatic diamines, were synthesized by a phosphorylation route using large amounts of triphenyl phosphite and pyridine as condensing reagents with stepwise addition of the condensing reagents. In the present polymers, [60]fullerene pearls and diamine linkers were attached to one another by cyclopropane connectors. The polyamides had weight-average molecular weights (M-w) of 4.5-5.0x10(4) g/mol and inherent viscosities (eta (inh)) of 0.3-0.4 dL/g in N,N-dimethylacetamide (DMAc) at 30 degreesC. They had glass transition temperatures at 30-125 degreesC and decomposition temperatures at 300-310 degreesC. The UV-VIS spectra in DMAc exhibited broad absorption with lambda (max) at 310-390 nm tailing to longer wavelengths. [References: 20]
机译：使用大量的亚磷酸三苯酯和吡啶作为缩合剂，并逐步添加缩合剂，通过磷酸化途径合成了一系列由赤道[60]富勒烯双乙酸和各种发色性芳香族二胺组成的[60]富勒烯珍珠项链聚酰胺。 。在本发明的聚合物中，[60]富勒烯珍珠和二胺连接基通过环丙烷连接基彼此连接。在30°C下的N，N-二甲基乙酰胺（DMAc）中，聚酰胺的重均分子量（Mw）为4.5-5.0x10（4）g / mol，固有粘度（eta（inh））为0.3-0.4 dL / g。 。它们的玻璃化转变温度为30-125℃，分解温度为300-310℃。 DMAc中的UV-VIS光谱表现出较宽的吸收率，在310-390 nm处的λ（最大值）拖到更长的波长。 [参考：20]