In this paper, the microwave heating has fabricated joints of stainless steel (SS). Ni-based powder (EWAC 1002 ET) is used to join the stainless steel. The characterization of joint has been carried out through microstructural analysis, X-ray diffraction analysis, tensile strength, elongation, and microhardness. Microstructure analysis reveals that the joint is clearly visible. There are no cracks at the joints. Very small amount of porosity has been observed. Hardness decreases toward the joint. As the exposure time and percentage of nickel-based powder increase, tensile strength also increases. Tensile strength, elongation, and microhardness of joint are 323.16MPa, 11.30%, and 145.3 Hv, respectively.
机译：在本文中，微波加热制造了不锈钢（SS）接头。镍基粉末（EWAC 1002 ET）用于连接不锈钢。通过微观结构分析，X射线衍射分析，抗张强度，伸长率和显微硬度对接头进行了表征。显微组织分析表明，该接头清晰可见。接头处无裂纹。已经观察到非常少的孔隙率。朝向接头的硬度降低。随着镍基粉末的暴露时间和百分比的增加，抗张强度也增加。接头的拉伸强度，伸长率和显微硬度分别为323.16MPa，11.30％和145.3 Hv。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号