首页> 外文期刊>Materials at High Temperatures >Evolution of the microstructure in a W alloy during sintering before the formation of a liquid phase
【24h】

Evolution of the microstructure in a W alloy during sintering before the formation of a liquid phase

机译：W合金在液相形成之前的烧结过程中微观组织的演变

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Partial densification in W-based alloysintering occurs before liquid phase formation by solidphase diffusion. During this step W diffuses in thesecond phase and tungsten grains connect between themto constitute a skeleton. A dilatometric study permitsto follow the shrinkage during heating. The secondphase, a Ni-based alloy NiFeCo, forms with tungsten aNiFeCoW alloy. The structure is that of nickel and thelattice parameter increases with increasing W content.Sintering tests are made from 5000C to 1,400℃ to knowthe solid phase range of W during liquid phase sintering.Limits of W% are determined until 1 ,4000C and are usedto define the diffusion temperature range. Theobservation of fracture surfaces gives the evolutionof the microstructure during the sintering and can becorrelated to diffusion results.
机译：W基合金烧结中的部分致密化发生在通过固相扩散形成液相之前。在该步骤期间，W在第二相中扩散并且钨晶粒在它们之间连接以构成骨架。膨胀计研究允许跟踪加热过程中的收缩。第二相是镍基合金NiFeCo，由钨aNiFeCoW合金形成。其结构为镍，晶格参数随W含量的增加而增加。在5000C至1,400℃的温度范围内进行烧结试验，以了解液相烧结过程中W的固相范围。确定W％的限量直至1,4000C并用于定义扩散温度范围。断裂表面的观察给出了烧结过程中微观结构的演变，并且可能与扩散结果有关。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号