首页> 外文期刊>Materials at High Temperatures >Predicting long-term creep-rupture property of Inconel 740 and 740H
【24h】

Predicting long-term creep-rupture property of Inconel 740 and 740H

机译：预测Inconel 740和740H的长期蠕变断裂性能

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The prediction of long-term creep-rupture strength values for Inconel 740 and 740H is made at temperatures ranging from 650 degrees C to 850 degrees C by using Larson-Miller (LM) and Manson-Haferd (MH) methodologies. Then, the predicted creep-rupture strength values are compared with the ones reported by Wilshire-Scharning (WS) model, a new approach for life assessment. The results show that the LM method is easy to cause either underestimation or overestimation of long-term properties depending on the selected data. Compared with the LM and WS methods, predictions produced by MH method have a relatively good consistency with the experimental data over 30 000 h, and the 105 hours creep-rupture strength extrapolated from rupture life of 5000 h or more than 30 000 h are almost same. This suggests that the MH method is a better method for predicting the long-term creep-rupture strength of Inconel 740 and 740H alloys.
机译：Inconel 740和740H的长期蠕变断裂强度值的预测是通过使用Larson-Miller（LM）和Manson-Haferd（MH）方法在650摄氏度至850摄氏度的温度范围内进行的。然后，将预测的蠕变断裂强度值与寿命评估的新方法Wilshire-Scharning（WS）模型报告的值进行比较。结果表明，LM方法很容易导致长期特性的低估或高估，具体取决于所选数据。与LM和WS方法相比，MH方法得出的预测值与30 000 h以上的实验数据具有较好的一致性，从5000 h或30 000 h以上的断裂寿命推断出的105 h蠕变断裂强度几乎是相同。这表明MH方法是预测Inconel 740和740H合金的长期蠕变断裂强度的更好方法。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号